ASPHALT CEMENT GRADE
AC - 2.5
|
ASPHALT CEMENT GRADE AC – 2.5 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
25 ± 5 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
80 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
200 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
165 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
125 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
100 |
|
AC - 5
|
ASPHALT CEMENT GRADE AC – 5 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
50 ± 10 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
110 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
120 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
175 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
250 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
100 |
|
AC – 10
|
ASPHALT CEMENT GRADE AC – 10 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
100 ± 20 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
150 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
70 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
220 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
500 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
75 |
|
AC – 20
|
ASPHALT CEMENT GRADE AC – 20 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
200 ± 40 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
210 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
40 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
230 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
100 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
50 |
|
AC – 30
|
ASPHALT CEMENT GRADE AC – 30 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
300 ± 60 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
250 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
30 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
230 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
1500 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
40 |
|
AC – 40
|
ASPHALT CEMENT GRADE AC – 40 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
400 ± 80 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
300 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
20 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
230 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Absolute Viscosity @ 60 °C |
pa.s |
ASTM D 2170 |
|
2000 |
|
Viscosity Ratio@ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
25 |
|