VISCOSITY GRADE BITUMEN
VG 10
|
VISCOSITY GRADE BITUMEN VG-10 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
Poise |
ASTM D 2170 |
800 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
250 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
80 |
100 |
|
Softening Point |
°C |
ASTM D 36 |
40 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
220 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Viscosity Ratio @ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
45 |
|
VG-20
|
VISCOSITY GRADE BITUMEN VG-20 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
Poise |
ASTM D 2170 |
1600 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
300 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
60 |
80 |
|
Softening Point |
°C |
ASTM D 36 |
45 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
220 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Viscosity Ratio @ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
50 |
|
VG-30
|
VISCOSITY GRADE BITUMEN VG-30 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
Poise |
ASTM D 2170 |
2400 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
350 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
50 |
70 |
|
Softening Point |
°C |
ASTM D 36 |
47 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
220 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Viscosity Ratio @ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
40 |
|
VG-40
|
VISCOSITY GRADE BITUMEN VG-40 |
||||
|
PROPERTY |
UNIT |
TEST METHOD |
LIMIT |
|
|
|
|
|
MIN. |
MAX. |
|
Absolute Viscosity @ 60 °C |
Poise |
ASTM D 2170 |
3200 |
|
|
Kinematic Viscosity @ 135 °C |
mm2/s |
ASTM D 2170 |
400 |
|
|
Penetration @ 25 °C, 100 g, 5 s |
0.1mm |
ASTM D 5 |
40 |
60 |
|
Softening Point |
°C |
ASTM D 36 |
50 |
|
|
Flash Point (Cleveland Open Cup) |
°C |
ASTM D 92 |
220 |
|
|
Solubility in Trichloroethylene |
% |
ASTM D 2042 |
99 |
|
|
Spot Test |
— |
A.A.SH.T.O |
Negative |
|
|
THIN FILM OVEN TEST (TFOT) |
||||
|
Viscosity Ratio @ 60 °C |
% |
ASTM D 2170 |
|
4 |
|
Ductility @ 25 °C, 5 cm/min after TFOT |
cm |
ASTM D 113 |
25 |
|